Characteristics of RA95 glaze active zinc oxide

*High temperature melting effect: modified ammonium zinc, high thermal conductivity, high activity at high temperature, effectively reduce the glaze viscosity.

*Strong activity and good color development: it can replace 99% to 99.5% calcined zinc oxide with the ratio of 1:1, and the color development effect remains unchanged.

*Stable performance of glaze slurry: the flow rate is 11.5 seconds, the glaze slurry is not thixotropic, and the flow rate is stable after long time storage

*Cost effective: the cost of zinc oxide for glaze can be reduced by about 20%.

*Mature products: from 2019 to now, it has sold more than 25000 tons, and the market application feedback is good

*High compatibility of glaze: more than 80% of the mainstream glaze formulation in the market can be replaced by 1 to 1 or fine adjustment compatibility.

*Stable composition and environmental protection: in addition, it contains 0.3% sodium, 0.5% calcium, 0.4% magnesium and 0.6% silicon. The content of heavy metal is up to the standard of 0.04% for lead and 0.00009% for cadmium.

*With antibacterial effect: the particle diameter is 6.5 μ m, with the electronic structure of semiconductor catalyst. As a strong oxidant, it can complete the explanation of organic matter and kill bacteria and viruses.

When the general zinc oxide is heated to 600 degrees, it will appear dark yellow and reach the active state. Our zinc oxide at room temperature is dark yellow, in the active state. It can instantly melt, high thermal conductivity, high activity, effectively reduce the glaze viscosity. The flow rate is 11.5 seconds, the glaze slurry is not thixotropic, and the flow rate is stable after a long time.